| RoHSII : | The material is in compliance with EU directive 2011/65/EU (RoHS II) | Base material : | Cellulotic paper |
|---|---|---|---|
| Matrix resin : | Phenolic |
Color : | Brown |
| Mechanical Properties | Variant | TestMethod | Value | Unit |
|---|---|---|---|---|
| Flexural stress at rupture perpendicular to laminations | min | ISO 178 | 142,59 |
MPa |
| Apparent modulus of elasticity in flexure | min | ISO 178 | 9921 |
MPa |
| Compressive strength perpendicular to laminations | min | ISO 604 | 305,8 |
MPa |
| Impact strength (Charpy) parallel to laminations | min | ISO 179/3C | 13,7 |
kJ/m2 |
| Shearing strength parallel | min | VDE 0318/2 | 24,44 |
MPa |
| Tensile strength | min | ISO 527-4 | 158,2 |
MPa |
| Electrical Properties | ||||
| Electric strengthat 90°C in oil perpendicular to laminations | min | IEC 60243-1 | 3,25 |
kV/mm |
| Breakdown voltage at 90°C in oil parallel to laminations | min | IEC 60243-1 | 15
|
kV |
| Insulation resistance after immersion in water | min | IEC 60167 | 223 |
M Ω |
| Proof tracking index PTI | IEC 60112 | |||
| Comparative tracking index CTI | min | IEC 60112 | 120 |
CTI |
| Tracking and erosion resistance | min | IEC 60112 | Class | |
| Thermal Properties | ||||
| Thermal endurance | IEC 60216 | T.I. | ||
| Density | ISO 1183 | 1,454 |
g/cm3 | |
| Water absorption | max | ISO 62 | 118,10* |
mg |
| Note: | * for test specimens 50 x 50 x 10mm Test values are derived from an average type test |
| The data mentioned in this data sheet is after our knowledge correct, but we reserve the right to make changes without notice. |
| rev: 09/2021 |